What is Galvanizing?

Galvanizing is the process of applying a zinc coating to steel to provide a rust protection layer. Iron will readily react with oxygen to form iron oxide (rust), and the zinc layer forms a protective barrier around the iron to protect it and improve the longevity of the steel.

The two most common methods of galvanizing steel are Hot Dip and Electrostatic Galvanizing.

What is Hot Dip Galvanizing?

Hot Dip Galvanizing is the process of coating steel by directly dipping it into a bath of molten zinc. The steel will need to go through a series of steps to ensure complete coverage of a good quality zinc layer. The steps generally include:

Caustic Cleaning – The steel is cleaned with a caustic solution to remove any contamination including dirt, grime, oil, and grease.

Rinsing – A rinse to remove any caustic solution.

Acidic Cleaning – The steel is cleaned with an acidic solution to remove any remaining scale.

Rinse – A rinse to remove any acidic solution.

Flux or Inhibiter Addition – A flux or inhibiter is added to the cleaned steel surface which is allowed to dry. This both inhibits oxidation and aids in the adhesion of zinc to the steel.

Dipping – The steel is dipped into the molten zinc bath until the temperature of the steel reaches the temperature of the zinc bath.

Quenching – The hot, coated steel is quenched to reduce the temperature and ensure the zinc coating remains unblemished.

The product of Hot Dip Galvanizing provides a relatively thick zinc layer.

What is Electrostatic Galvanizing?

Electrostatic Galvanizing is the process of coating steel in zinc by using electroplating. This involves submerging the steel (which acts as a cathode) and an inert anode in an aqueous solution containing dissolved zinc salts. A current is then forced from the steel cathode, through the aqueous zinc solution, and to the inert anode. By forcing this electric current through the steel, the dissolved zinc is plated on top of the steel and provides a complete barrier.

The product of Electrostatic Galvanizing will provide a relatively thin zinc layer.

What are the advantages and disadvantages of both methods?

While the hot dip and electrostatic galvanizing methods differ considerably, the differences in the final product can be summarized into three key areas.

Cost – Hot Dip Galvanizing is the cheaper of the two methods as this process is typically better for mass production. Electrostatic galvanizing tends to be used for more specialized applications. In many applications, the cost factor will be the deciding factor on choosing the type of galvanizing to be used.

Appearance – The two methods produce final galvanized products that look vastly different. Hot dipped galvanized products tend to be dull, uneven and can look rough. Electrostatic galvanizing produces an excellent final finish as the coating is very uniform, smooth, and shiny. If appearances are important for an application, then electrostatic galvanizing may be the preferred option.

Galvanizing layer thickness – The thickness of a both types of galvanized coating can be controlled and varied, although typically the Hot Dipped Galvanized coating would be around 80 to 100µm, while the electrostatic galvanizing typically produces a coating of around 10 to 12µ This means if longevity is the biggest concern, then hot dip galvanizing will be the preferred option as it provides a thicker protection layer and a typical lifetime of decades. A thicker coating can be a disadvantage in steel with small tolerances or threads.

What are Common Applications for each Method?

Hot Dip Galvanized products are used in almost any application that benefits from a low production cost and a long life. This is especially relevant for any steel products that will be exposed to the weather. Typical examples include:


Support steel



Electrostatic Galvanizing tends to be utilized for more specialized purposes that require a smooth finish or tight tolerances. These include:

Steel plating (as used in the automotive industry)


Small parts (as used in appliances)

Channel is a structural metal that has many different applications across several industries.

It is a common building and construction material. It also used in the ship building and automotive industries, and general fabrication where structural properties are required. The C- or U-shape lend well to structural applications where the load is focused vertically or horizontally.

If laid flat, Channel can be measured by taking the width of the channels, the height of its Flange (legs) and Web (thickness of the material between the two flanges).

Channel is available in the following metal types:


Mild Steel

Stainless Steel

Channel can be purchased online and at any Metal Supermarkets location. It can be cut to your exact specifications.

Galvanized c channel refers to a new type of high-strength steel plate, which is cold-formed and roll-formed. It has a uniform wall thickness, excellent cross-sectional performance, and high strength. Compared with traditional hot rolling, it can save 30% of the material.

Hot Selling Steel Galvanized C Channel Description:

Product Name: Hot Selling Steel Galvanized C channel

Keywords:Galvanized c Channel, Steel c Channel

Standards: GB

Material: Q195

Size: 80x40x20x2.5mm

Thickness: 2.5mm

Length: 2.44m-6m or as customer required

Type: C shaped

Technology: Galvanized

Surface treatment: Oil /Black/painting or zinc coating

Application: construction/welding /greenhouse or water system

The main advantages of steel c channel are:

1. Durability: In urban areas or offshore areas, the standard hot-dip galvanized antirust layer can be used for 20 years; in the suburbs, it can be used for more than 50 years.

2. Comprehensive protection: Each part can be plated with zinc, which is fully protected.

3. The toughness of the coating is strong: it can withstand mechanical damage during transportation and use.

4. Good reliability.

5. Save time and effort: The galvanizing process is faster than other coating construction methods and can avoid the time required to paint on the construction site after installation.

6. Low cost: galvanizing is more expensive than spray painting, but in the long run, the cost of galvanizing is low, because the durability of galvanizing is long-lasting.

Galvanized c channel, uniform zinc layer, smooth surface, strong adhesion, high dimensional accuracy, all surfaces are wrapped by zinc layer, surface zinc content is usually 120-275g / ㎡, long service life, corrosion resistance, durable, protection The strongest kind of galvanized c channel with high quality.


23rd, Floors, Science and Technology Finance Buildling. No.5, Meiyuan Road, Xiqing District, Tianjin,China.


Sino Green New Energy Tech Co Ltd